ZC-SC125P 125℃ Self-crosslinking LSZH FR Polyolefin Material for Solar Cable

Basic Information
Place of Origin: China
Brand Name: Zion communication OR OEM
Certification: CE,RoHS, VDE,UL,CUL,LPCB
Model Number: Solar cable
Minimum Order Quantity: 1,000 PCS
Packaging Details: Carton
Delivery Time: Normally 15 days
Payment Terms: T/T,L/C
Supply Ability: 10*20’GP/Month
Detail Information
Standard: EN50618-2014 Specifications: Wires And Cables Up To 3KV.
Net Weight: 25kg And B Component Is 5kg Environment: Clean, Dry And Ventilated Warehouses
Warranty: 6 Months
High Light:

coax cable connectors

,

tv coaxial cable connectors


Product Description

125℃ Self-cross linking LSZH FRPolyolein Cable Compound
ZC-SC125P
General lnformation
Description
ZC-SC125P is a self-crosslinking low smoke zero halogen flame retardant polyolefin cable compound, which can be naturally cross-linked after being extruded into a cable. This product is mainly used for the sheath and insulation of photovoltaic cables that comply with TUV2Pfg-1169 and EN50618.
 
Standard
1) EN50618-2014
2) 2Pfg1169/08-2007
3) IEC60332-1-2-2015
 
Specifications
High temperature resistance XLPO Compound for wires and cables up to 3KV.
 
Specification Sheet
Product Properties
  Unit Test method Standard
Value
Typical
Value
    Nation International
Density g/cm3 GB/T 1033 ISO 1183-1 1.40
Tensile strength Mpa GB/T 1040.2 ISO 527-2 ≥10.0 13.5
Elongation at break % ≥150 250
Air ageing
(158±2℃,
168h)
Change of
tensile strength
% GB/T 2951.12 IEC 60811-1 ±25 +12
Change of
elongation
% ±25 -8
Volume resistivity (20℃) Ω·m GB/T 1410 IEC 60093 ≥1.0x1012 2.6x1012
Volume resistivity at operating temperature (125±2℃) Ω·m ≥2.0x108 3.5x108
Dielectric strength MV/m GB/T 1408.1 IEC 60243-1 ≥20 25
Brittleness temperature (-40℃) ℃) GB/T 5470 ISO 974 Pass Pass
Hot set
elongation
(200℃,
0.2Mpa,
15min)
Elongation
under load
% GB/T 2951.21 IEC
60811-2-1
≤100 45
Permanent
deformation
% ≤25 0
Water
Immersion test
(70℃, 168h)
Change of
tensile strength
% GB/T 32129 ±30 -3
Change of
elongation
% ±35 -6
                               
Product Properties
  Unit Test method Standard
Value
Typical
Value
    Nation International
Oxygen index % GB/T 2406.2 ISO 4589-2 ≥28 35
Smoke
density
non-luminous flame   GB/T 8323.2 ISO 5659-2 ≤350 310
flame combustion ≤100 70
HCl and HBr content % GB/T 17650 IEC 60754 ≤0.5 0
HF content % ≤0.1 0
pH value ≥4.3 5.0
Conductivity μS/mm ≤10 1.1
                               
NOTE: (1)The toxicity of smoke produced by materials shall be negotiated by both the supplier and the demander
according to the needs of the product application.
(2)Thetechnicalindicatorsspecifiedinthetablearethevaluesobtainedaftercrosslinking.
Additional Information
Processing Techniques:
Extruding techniques
It is recommended to use a low smoke zero halogen special screw, with a length to diameter ratio of L/D=20~25 and a compression ratio of 1.1~1.3. Because the actual temperature of the melt is related to the length diameter ratio, compression ratio and screw structure of the extruder, the appropriate extrusion temperature should be selected according to the specific situation of the extruder.
The recommended setting temperatures for each zone of the extruder are as follows:
Zone Z1 Z2 Z3 Z4 Head Die
Temperature(℃) 120 130 140 140 150 150
 
Using
(1)When using this product, mix the A and B components evenly and drop them into the hopper.
If color is required, the cable factory can use polyethylene base color masterbatch and materials
within 8 hours after unpacking.
(2)This product should not be shut down for a long time. If it is shut down for a long time, it is
recommended to stop and clean the screw before starting up again.
(3)To ensure sufficient crosslinking of the material, it is recommended that the cable be placed in
a 70°C water bath or steam room for 6~8h, or at a constant temperature and humidity (23°C, 50%)
for 7 days. The specific placement time is adjusted according to the thickness of the product and
the crosslinking degree of the material, so as to meet the performance requirements of the cable.
Package.Storage and Transport:
Package Net weight The A and B component are kept in different bags, net weight of
A component is 25kg and B component is 5kg
Method Aluminum foil/polyethylene complex film bag for inner+ PP woven bag/
PE/Kraft paper bag for outer
Transport Requirement Keep away from the sunshine, rain and soaking during transport, as well
as handle gently during carrying.
Storage Environment clean, dry and ventilated warehouses
Warranty 6 months

 