125℃ Self-cross linking LSZH FRPolyolein Cable Compound
ZC-SC125P

General lnformation

Description

ZC-SC125P is a self-crosslinking low smoke zero halogen flame retardant polyolefin cable compound, which can be naturally cross-linked after being extruded into a cable. This product is mainly used for the sheath and insulation of photovoltaic cables that comply with TUV2Pfg-1169 and EN50618.

Standard

1) EN50618-2014

2) 2Pfg1169/08-2007

3) IEC60332-1-2-2015

Specifications

High temperature resistance XLPO Compound for wires and cables up to 3KV.

Specification Sheet

Product Properties

Unit

Test method

Standard
Value

Typical
Value

Nation

International

Density

g/cm³

GB/T 1033

ISO 1183-1

┄

1.40

Tensile strength

Mpa

GB/T 1040.2

ISO 527-2

≥10.0

13.5

Elongation at break

≥150

250

Air ageing
(158±2℃,
168h)

Change of
tensile strength

GB/T 2951.12

IEC 60811-1

±25

+12

Change of
elongation

±25

-8

Volume resistivity (20℃)

Ω·m

GB/T 1410

IEC 60093

≥1.0x10¹²

2.6x10¹²

Volume resistivity at operating temperature (125±2℃)

Ω·m

┄

≥2.0x10⁸

3.5x10⁸

Dielectric strength

MV/m

GB/T 1408.1

IEC 60243-1

≥20

Brittleness temperature (-40℃)

℃)

GB/T 5470

ISO 974

Pass

Hot set
elongation
(200℃,
0.2Mpa,
15min)

Elongation
under load

GB/T 2951.21

IEC
60811-2-1

≤100

Permanent
deformation

≤25

Water
Immersion test
(70℃, 168h)

Change of
tensile strength

GB/T 32129

┄

±30

-3

Change of
elongation

±35

-6

Product Properties

Unit

Test method

Standard
Value

Typical
Value

Nation

International

Oxygen index

GB/T 2406.2

ISO 4589-2

≥28

Smoke
density

non-luminous flame

GB/T 8323.2

ISO 5659-2

≤350

310

flame combustion

≤100

HCl and HBr content

GB/T 17650

IEC 60754

≤0.5

HF content

≤0.1

pH value

┄

≥4.3

5.0

Conductivity

μS/mm

≤10

1.1

NOTE: (1)The toxicity of smoke produced by materials shall be negotiated by both the supplier and the demander
according to the needs of the product application.
(2)Thetechnicalindicatorsspecifiedinthetablearethevaluesobtainedaftercrosslinking.

Additional Information

Processing Techniques:

Extruding techniques
It is recommended to use a low smoke zero halogen special screw, with a length to diameter ratio of L/D=20~25 and a compression ratio of 1.1~1.3. Because the actual temperature of the melt is related to the length diameter ratio, compression ratio and screw structure of the extruder, the appropriate extrusion temperature should be selected according to the specific situation of the extruder.
The recommended setting temperatures for each zone of the extruder are as follows:

Zone

Head

Die

Temperature(℃)

120

130

140

150

Using

(1)When using this product, mix the A and B components evenly and drop them into the hopper.
If color is required, the cable factory can use polyethylene base color masterbatch and materials
within 8 hours after unpacking.
(2)This product should not be shut down for a long time. If it is shut down for a long time, it is
recommended to stop and clean the screw before starting up again.
(3)To ensure sufficient crosslinking of the material, it is recommended that the cable be placed in
a 70°C water bath or steam room for 6~8h, or at a constant temperature and humidity (23°C, 50%)
for 7 days. The specific placement time is adjusted according to the thickness of the product and
the crosslinking degree of the material, so as to meet the performance requirements of the cable.

Package.Storage and Transport:

Package

Net weight

The A and B component are kept in different bags, net weight of
A component is 25kg and B component is 5kg

Method

Aluminum foil/polyethylene complex film bag for inner+ PP woven bag/
PE/Kraft paper bag for outer

Transport

Requirement

Keep away from the sunshine, rain and soaking during transport, as well
as handle gently during carrying.

Storage

Environment

clean, dry and ventilated warehouses

Warranty

6 months

Tag:

Place of Origin:	China
Brand Name:	Zion communication OR OEM
Certification:	CE,RoHS, VDE,UL,CUL,LPCB
Model Number:	Solar cable

Minimum Order Quantity:	1,000 PCS
Packaging Details:	Carton
Delivery Time:	Normally 15 days
Payment Terms:	T/T,L/C
Supply Ability:	10*20’GP/Month

ZC-SC125P 125℃ Self-crosslinking LSZH FR Polyolefin Material for Solar Cable

coax cable connectors

tv coaxial cable connectors

coax cable connectors,

female coaxial connector,

tv coaxial cable connectors

TC Tinned Copper Wire For Electronic Components / Circuit Boards

Bending Resistance LSZH Compound For Motor Wire Insulation / Sheath

Locomotive Cable Sheath LSZH Compound For Subway And High Speed Railway

LSZH Compound For Insulation And Sheath Of Photovoltaic Cable

Solid Insulation Of Power Cord PE Compound Cable Material

Insulation Sheath LSZH Compound For Building Wire And Power Cord

Flame Retardant PE Compound Raw Materials For High Voltage Power Cable

PE Compound For Power Cable Sheath / Submarine Cable Sheath