Name: ZC-SC101H XLPO Material for Solar Cable
Brand: Zion communication OR OEM
SKU: Solar cable
Rating: 4.9 (165 reviews)

Detail Information

Application:	Insulation Of Solar Cables	Specifications:	Wires And Cables Up To 3KV.
Tensile Strength:	ISO 527:1995,	Elongation At Break:	450%
Elongation Under Load:	50%
Highlight:	tv coaxial cable connectors , female coaxial connector

Product Description

ZC-SC101H

General lnformation

Description

It is a type of warm water cross linking material applied to low voltage wires and cables.
It possesses following advantage: good electrical properties and anti-aging ability;
excellent tensilestrength and low-temperature brittleness properties. In addition,
the highest continuous workingtemperature is 125℃.
This grade is compliant to EN 50618 and passed all properties except the20,000 hours aging test.

Application:

it is used for the insulation of solar cables

Specifications

High temperature resistance XLPO Compound for wires and cables up to 3KV.

Specification Sheet

Product Properties

Unit

Test method

Standard
Value

Typical
Value

Nation

International

Physical

Gel content

GB/T 10437-2004

┄

Density

g/cm³

ASTMD 792

0.917

Mechanical

Tensile strength

Mpa

GB/T 1040-2006

ISO 527:1995,

┄

Elongation at break

IDT

┄

450

Brittleness temperature
(-76℃,30pieces)

Piece

GB/T 5470-2008

ISO 974:2000

┄

MOD

Thermal

Hot set
elongation
(200℃,
0.2Mpa,
15min)

Elongation
under load

GB/T2951.21-2008

IEC
60811-2-1:2001,
IDT

┄

Permanent
deformation
after cooling

┄

Ageing
(150℃,
240h)

Change of
tensile strength

GB/T2951.12-1997

IEC
60811-2-1:2001,
IDT

┄

Change of
elongation

┄

Product Properties

Unit

Test method

Standard
Value

Typical
Value

Nation

International

Thermal

DC volume resistivity (20℃)

Ω·m

GB/T 1410-2006

ISO 60093:1980

┄

1.0x10¹⁵

IDT

Dielectric Strength (20℃)

MV/m

GB/T 1408.1-1999

IEC 602431:1998

┄

IDT

Dielectric constant (20℃,50HZ)

┄

GB/T 1409

IEC 60250:1969,
MOD

┄

2.20

Dissipation factor (20℃,50HZ)

┄

30x10^-4

Additional Information

Processing Techniques:

Melt extrusion temperature in the range of 150℃ to 220℃ are recommended, the specifictemperature
should be adjusted by actual operation condition.

Cross-linking:

Cross-linking condition and time of the hot set elongation to 100%(1mm thick samples);vapor or water bath
at 90℃ for 6Omin or at 80℃ for 120min.

Package.Storage and Transport:

Package

Net weight

the A and B groups are kept in different bags, net weight ofA group is
( 23.75土0.02) kg and B group ( 1.25+0.02) kg

Method

aluminium foil / polyethylene complex film bag for inner+
PP woven bag/PE/ Kraft paper bag for outer

Transport

Requirement

keep away from the sunshine, rain and soaking duringtransport,
as well as handle gently during carrying

Storage

Environment

clean, dry and ventilated warehouses

Warranty

6 months

Tag:

Place of Origin:	China
Brand Name:	Zion communication OR OEM
Certification:	CE,RoHS, VDE,UL,CUL,LPCB
Model Number:	Solar cable

Minimum Order Quantity:	1,000 PCS
Packaging Details:	Carton
Delivery Time:	Normally 15 days
Payment Terms:	T/T,L/C
Supply Ability:	10*20’GP/Month

ZC-SC101H XLPO Material for Solar Cable

tv coaxial cable connectors

female coaxial connector

coax cable connectors,

female coaxial connector,

tv coaxial cable connectors

TC Tinned Copper Wire For Electronic Components / Circuit Boards

Bending Resistance LSZH Compound For Motor Wire Insulation / Sheath

Locomotive Cable Sheath LSZH Compound For Subway And High Speed Railway

LSZH Compound For Insulation And Sheath Of Photovoltaic Cable

Solid Insulation Of Power Cord PE Compound Cable Material

Insulation Sheath LSZH Compound For Building Wire And Power Cord

Flame Retardant PE Compound Raw Materials For High Voltage Power Cable

PE Compound For Power Cable Sheath / Submarine Cable Sheath